一、相关技术参数 |
|
|
|
|
|
|
|
规格 |
800M |
1250M |
2000M |
2500M |
3000M |
||
Bags Numbers 包装袋编号 |
AT-0023 |
AT-0026 |
AT-0028 |
AT-0030 |
AT-0036 |
||
粒径(10μm)分布通过累计重量（%） Pateicle size distribution |
1.0μm |
25 |
30 |
45 |
50 |
60 |
|
2.0μm |
40 |
50 |
70 |
85 |
95 |
||
5.0μm |
60 |
70 |
95 |
97 |
99 |
||
8.0μm |
75 |
85 |
97 |
98 |
100 |
||
10 μm |
85 |
97 |
99 |
100 |
|
||
16 μm |
97 |
99 |
100 |
|
|
||
20 μm |
99 |
100 |
|
|
|
||
30 μm |
100 |
|
|
|
|
||
Particle Size |
粒径D50(μm)≤ |
3 |
2 |
1.3 |
1 |
0.8 |
|
Particle Size |
粒径D97(μm)≤ |
16 |
10 |
6 |
5 |
4 |
|
Appearance |
外观 |
白色粉末 |
白色粉末 |
白色粉末 |
白色粉末 |
白色粉末 |
|
Whiteness |
白度%≥ |
93 |
95 |
96 |
96 |
96 |
|
Sieve Test |
筛余物(20μm)≤ |
0.8 |
0.1 |
0 |
0 |
0 |
|
PH Value |
PH值 |
8.5～9.5 |
8.5～9.5 |
8.5～9.5 |
8.5～9.5 |
8.5～9.5 |
|
Oil Absorption |
吸油量(ml/100g) |
18～22 |
22～24 |
22～30 |
22～30 |
30～40 |
|
Moisture Content |
水份%≤ |
0.5 |
0.5 |
0.5 |
0.5 |
0.5 |
|
Mobility Extent |
活化度% |
95 |
95 |
95 |
95 |
95 |
|
DOP Absorption value |
DOP吸油量(ml/100g) |
40～45 |
42～50 |
48～58 |
50～60 |
60～65 |
|
Loss on lgnition |
烧失量% |
43.5 |
43.5 |
43.5 |
43.5 |
43.5 |
|
Sediment Volume |
沉降体积（ml) |
30 |
35 |
55 |
60 |
68 |
|
True Specific Gravity |
真比重（t/m3) |
2.7 |
2.7 |
2.7 |
2.7 |
2.7 |
|
Postulate Specific Gravity |
假比重（t/m3) |
1 |
0.85 |
0.7 |
0.6 |
0.5 |
|
CaCO3 |
碳酸钙%≥ |
98.8 |
98.8 |
98.8 |
98.8 |
98.8 |
|
Fe2O3 |
三氧化二铁%≤ |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
|
SiO2 |
二氧化硅%≤ |
0.01 |
0.01 |
0.01 |
0.01 |
0.01 |
|
MgO |
氧化镁%≤ |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
|
Al2O3 |
三氧化二铝%≤ |
0.01 |
0.01 |
0.01 |
0.01 |
0.01 |
|
二 、产品主要作用
在造纸行业使用，具有增加表面光泽，提高白度、改善纸张表面平滑度等要求。
在橡胶行业使用：可提高产品的拉伸、抗张、耐热、耐老化、耐撕裂等性能。
在涂料行业中使用：可以增加涂膜厚度，提高涂层的耐磨性和耐候性，同时可提高粉末涂料的上粉率和喷涂面积，另外它不含重金属，是不含重金属类粉末涂料的首选填料。